UNS S17400 Precipitation Hardening Stainless Steel Bar Chromium Nickel Copper Martensitic Stainless Steel

Contact Now
BLOOM(suzhou) Materials Co.,Ltd
Visit Website
Province/State:jiangsu
Country/Region:china
Contact Person:MrsKara Liu
Contact Now

UNS S17400 Precipitation Hardening Stainless Steel Bar Chromium Nickel Copper Martensitic Stainless Steel

Ask Latest Price
Brand Name :BLM-1H-1
Place of Origin :Jiangsu, China (Mainland)
MOQ :100kgs
Price :FobShanghai usd 2.8-6.0/kg
Payment Terms :Western Union, L/C, T/T
Supply Ability :300 Ton/Tons per Month
Delivery Time :25-30 days subject to the clients' requirement and quantity
Packaging Details :packed and labeled according to the regulations and customer's requests.Great care is taken to avoid any damage which might otherwise be caused during storage or transportation.
Standard :AISI, ASTM, BS, DIN, GB, JIS, Other,JIS,AISI,ASTM,GB,DIN,EN
Grade :17-4PH
Type :Bar
Dimensions :10-900MM
Length :2m,3m or as required
Special Use :Cold Drawn
Delivery :25-30 days subject to the clients' requirements and quantity
Price Term :Ex-Work,FOB,CNF,CFR,CIF,FCA,DDP,DDU
Surface Treatment :bright&smooth
more
Contact Now

Add to Cart

Find Similar Videos
Bimetallic / Nitrided Conical Twin Screw Barrel For Extruder 00:34
Bimetallic / Nitrided Conical Twin Screw Barrel For Extruder
Corrosion Resistant Bimetallic Screw Elements And Barrel For Plastic Extruder Of Masterbatch Fluororubber 00:39
Corrosion Resistant Bimetallic Screw Elements And Barrel For Plastic Extruder Of Masterbatch Fluororubber
Si3N4 Silicon Carbide Nitride Ceramic Groove Tube Rod Pins Customization 00:17
Si3N4 Silicon Carbide Nitride Ceramic Groove Tube Rod Pins Customization
Spot Welding Machine Electrode Arm Chromium Zirconium Copper Special Shaped 00:20
Spot Welding Machine Electrode Arm Chromium Zirconium Copper Special Shaped
Type 75 Twin Screw Extruder Elements For Engineering Plastic Extruder Spare Parts 00:53
Type 75 Twin Screw Extruder Elements For Engineering Plastic Extruder Spare Parts
Spot Welding Tip Remover Electrode Wrench 8 - 25mm Dia 00:30
Spot Welding Tip Remover Electrode Wrench 8 - 25mm Dia
Industrial Black KCF Sleeve For Bolt Welding Size M5 M6 M8 M10 M12 00:19
Industrial Black KCF Sleeve For Bolt Welding Size M5 M6 M8 M10 M12
Pneumatic Tip Dresser 13D / 16D With One Holder And One Cutter Blade 00:22
Pneumatic Tip Dresser 13D / 16D With One Holder And One Cutter Blade
KTW Ratchet Type Handheld Tip Dresser For Spot Welding 00:24
KTW Ratchet Type Handheld Tip Dresser For Spot Welding
Parallel Twin Screw Barrel For Inflating Food Extruder Double Co Rotation Screws 00:46
Parallel Twin Screw Barrel For Inflating Food Extruder Double Co Rotation Screws
View Product Description

Machined The Solution Treated and Precipitation Hardened Conditions 17-4ph Bar

1 . Descriptions:

Alloy 17-4PH (UNS S17400), Type 630, is a chromium-nickel-copper precipitation-hardening martensitic stainless steel with an addition of niobium. 17-4PH combines high strength and hardness with good corrosion resistance. The alloy is furnished in the solution annealed condition (Condition A). It should not be used at temperatures above 572°F (300°C) or for cryogenic service. Optimal mechanical properties can be obtained by subjecting the alloy to age hardening heat treatments. Heat treatment in the 900°F (482°C) range produces the highest strength. The corrosion resistance of Alloy 17-4PH is comparable to 304 stainless steel in most environments, and is generally superior to the 400 series stainless steels. It is used in applications where the combination of moderate corrosion resistance and unusually high strength are required. Alloy 17-4PH can be easily welded and processed by standard shop fabrication practices. It is magnetic.

2 . Chemical Composition:

Grade Standard C Si Mn P S Cr Ni Cu Nb
630 ASTM A564 ≤0.07 ≤1.0 ≤1.0 ≤0.04 ≤0.03 15.0~17.0 3.0~5.0 3.0~5.0 0.15~0.45

3 . Mechanical Properties:

CONDITION AS-BUILT² AFTER POST HEAT TREATMENT³
Ultimate Tensile Strength, MPa ASTM E8 1100 ± 50 1300 ± 50
Yield Strength, MPa ASTM E8 620 ± 30 1100 ± 50
Elongation at break, % ASTM E8 16 ± 2.0 10 ± 2.0
Hardness 300 ± 20 HV5 400 ± 20 HV5
Density approx. 100%

4 . Applications:

can be machined in both the solution treated and
precipitation hardened conditions. Machining characteristics may vary according to the hardness of the
metal. High speed tools are acceptable, but carbide tools are preferred. Standard lubrication should be used. Dimensional changes as a result heat treatment should be taken into account if very stringent tolerances are required.

• Aerospace  —  structural and parts
• Biomedical  —  hand tools
• Chemical Processing
• Food Process Equipment
• Gate Valves
• Mechanical Components
• Oil and Gas Production  —  foils, helicopter deck platforms, etc.
• Pulp and Paper  —  paper mill equipment

5 . Features:

  • High tensile strength and hardness to 600°F
  • Corrosion resistant
  • Excellent oxidation resistance to about 1100°F
  • Creep-rupture strength to 900°F

6 . More pictures

UNS S17400 Precipitation Hardening Stainless Steel Bar Chromium Nickel Copper Martensitic Stainless Steel


Inquiry Cart 0
You May Like
15-5 PH Bar Precipitation Hardening Stainless Steel UNS S15500 Grade For Nuclear Waste Casks
15-5 PH Bar Precipitation Hardening Stainless Steel UNS S15500 Grade For Nuclear Waste Casks
High Toughness 17 4 Steel Plate , 17 4ph Plate For Shaft And Bearing
High Toughness 17 4 Steel Plate , 17 4ph Plate For Shaft And Bearing
06Cr18Ni11Ti Precipitation Hardening Stainless Steel Wire High Hardness For Pulp And Paper Industry
06Cr18Ni11Ti Precipitation Hardening Stainless Steel Wire High Hardness For Pulp And Paper Industry
Precipitation Hardening Stainless Steel Tube With Excellent Formability And Weldability
Precipitation Hardening Stainless Steel Tube With Excellent Formability And Weldability
Uns S17400 17 4PH Material , 1704 Stainless Steel Customized Length
Uns S17400 17 4PH Material , 1704 Stainless Steel Customized Length
UNS S15500 Grade 15 5 Ph Alloy Plate ASTM Standard For Aviation Field
UNS S15500 Grade 15 5 Ph Alloy Plate ASTM Standard For Aviation Field
15-5 PH Wire Precipitation Hardening Stainless Steel 10-900MM Dimensions With High Hardness
15-5 PH Wire Precipitation Hardening Stainless Steel 10-900MM Dimensions With High Hardness
Hot Rolled 15 5 PH Stainless Steel Pipe , Steel & Alloy Bar With Polished Surface
Hot Rolled 15 5 PH Stainless Steel Pipe , Steel & Alloy Bar With Polished Surface
Low Carbon Content 17 7PH Plate With Superior Weldability 0.282 Lb / Inch3 Density
Low Carbon Content 17 7PH Plate With Superior Weldability 0.282 Lb / Inch3 Density
Corrosion Resistant Precipitation Hardening Stainless Steel , 17 7PH Tube For Pump Shafts Industries
Corrosion Resistant Precipitation Hardening Stainless Steel , 17 7PH Tube For Pump Shafts Industries
17 7PH Strip Precipitation Hardening Stainless Steel Round Bar H9 H10 H11 Tolerance 1m-6m Length
17 7PH Strip Precipitation Hardening Stainless Steel Round Bar H9 H10 H11 Tolerance 1m-6m Length
EN10088-1 Precipitation Hardening Steel 17-7PH Nickel Alloy Cold Drawn Bar
EN10088-1 Precipitation Hardening Steel 17-7PH Nickel Alloy Cold Drawn Bar
Hot Steel 17-4PH Forging Parts Roll Rings Cold Drawn
Hot Steel 17-4PH Forging Parts Roll Rings Cold Drawn
Rod Type 17 7 Ph Hardened Steel Rod With Excellent Mechanical Properties
Rod Type 17 7 Ph Hardened Steel Rod With Excellent Mechanical Properties
Wire Type Precipitation Hardening Stainless Steel With Excellent Corrosion Resistance 0.01-15mm Dia
Wire Type Precipitation Hardening Stainless Steel With Excellent Corrosion Resistance 0.01-15mm Dia
Send your message to this supplier
*From:
*To:

BLOOM(suzhou) Materials Co.,Ltd

*Subject:
*Message:
Characters Remaining : (0/3000)
Contact Now